Features

Benefits

Thermal stability

Resists steam or continuous hot-water cleaning

Fast curing

Minimizes down time

Solvent free

Low odor; VOC compliant

No priming or sealing of substrate

Single-lift application

30 years of project references

Proven track record

Can be applied to 7-10 day old properly prepared concrete

Accelerates work schedules

Extremely high bond strength

Reduces shear at bond line

Chemical resistant

Tolerates organic and inorganic acids, alkalis and salts

Unaffected by freeze/thaw cycles

Handles wide temperature fluctuations

Wide temperature in-service range from -50° to 235° F (-45 to 112° C)

Exceeds that of typical epoxy overlays

Excellent impact and abrasion resistance

Handles heavy traffic

Coefficient of thermal expansion similar to concrete

Prevents shear at bond line

Slip resistant

Meets ADA recommendations

Test Data:  System Performance Properties

Compressive strength, psi (MPa)

ASTM C 579

7,300 (50.3)

Tensile strength, psi (MPa)

ASTM C 307

800 (5.5)

Coefficient of thermal

expansion, in/in/°F (cm/cm/°C)

ASTM C 531

1.1 x 10ˉⁿ [n=5], (2.0 x 10ˉⁿ [n=5])

Density, lb/ft³ (g/cm³)

ASTM C 905

130 (2.80)

Resistance to fungi growth

ASTM G 21

Passes, rating of one

Impact resistance

ASTM D 2794

No visible damage or deterioration at minimum 160 in-lb

Compressive modulus, psi (MPa)

ASTM C 469

1.7 x 10ⁿ [n=5] (1,170)

Flexural strength

ASTM C 580

1,800 (12.4)

Modulus of elasticity, psi (MPa)

ASTM C 469

1.7 x 10ⁿ [n=5] (1,170)

Thermal conductivity,

BTU-in/in-ft² °F (W/mK)

ASTM C 177

8 (1.2)

Water absorption, %

ASTM C 413

< 0.1

Abrasion resistance, g loss;

CS-17 Wheel, 1,000 cycles

ASTM C 4060

0.07

Resistance to elevated temperatures

MIL-D-3134

No flow or softening

Adhesion, psi (MPa)

ASTM D 4541

400 (2.8) 100% concrete failure

Coefficient of friction, wet and dry

ASTM D 2047

Passes ADA recommendations